08F(1008)/10F(1010) Low carbon cold rolled sheet
Cold rolled steel is the steel produced by cold rolling, under certain conditions, the steel plate can be further pressed into the required thickness, it and hot pressed steel plate compared, the thickness will be more accurate, and the surface is more smooth and more beautiful. At the same time, it also maintains stable performance, such as processing skills are very good, but they are not suitable for processing, so they need to be handed over to customers by annealing.

Product details

08F(1008) is a grade of boiling steel in stamping steel plates, F refers to boiling steel, 08 refers to the carbon content of eight parts per million.08F characteristics: low strength and hardness, plasticity, toughness, easy to deep drawing, drawing, bending and welding.

10F(1010) steel is a high-quality carbon steel, plastic, stamping and other cold processing and welding performance is good.


Product information:

Name

08F(1008)/10F(1010) Low carbon cold rolled sheet

Alloy Or Not

Non-Alloy

Production Process

Cold Rolling

Material Standards

AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc.

Width

500mm,1000mm,1250mm,3000mm,Or customized Size

Length

1m-12m, or Customized Size

Thickness

0.3-3mm

Delivery Conditions

Rolling, Annealing, Quenching, Tempered or Standard

Standard:

AiSi, ASTM, bs, DIN, GB, JIS

Certificate

CE, tisi, KS, JIS, GS, ISO9001

Delivery Time

within 3-5 days


x-cold-1.jpg

08F  Chemical composition(%): (C)0.05-0.11, (Cr)≤0.10,(Mn)0.25-0.50,(Ni)≤0.30,(Si)≤0.03,(P)≤0.035,(S)≤0.035,(Cu)≤0.20

Mechanical properties:

Section shrinkage ratio ψ (%):≥60

Hardness: No heat treatment, ≤131HB

In 08F, F means boiling steel, and 08 means that the carbon content is eight parts per 10,000

08F steel has good plasticity and is mainly used to manufacture cold stamping parts. Manganese plays a role in increasing elastic strength in steel, so the content can be deviated under the condition that the requirements are met.

---------------------------------------------------------------------------------------------------------------------------

10F Chemical composition(%): (C):0.07-0.13,(Mn):0.25-0.50, (Cr):≤0.15, (Ni):≤0.30, (Si):≤0.07, (Cu):≤0.25.

Mechanical property:

Section shrinkage ratio ψ (%):≥55;

Hardness: no heat treatment, ≤137HB;

Tensile strength σb (MPa):≥315(32);

Yield strength σs (MPa):≥185(19);

Elongation δ5 (%):≥33.

10F steel is high quality carbon steel. This steel strength is not large, and the difference state plasticity and toughness is very high, has good stamping, tensile and bending properties, good weldability, can be used for plastic parts: gaskets, strength requirements are not high carburizing and cyanide parts; Sleeve, short shaft, clutch disc.

WORKSHOP EQUIPMENT

The company mainly produces hot rolled steel plate, cold rolled steel plate, carbon steel coil, carbon steel pipe, API pipe, structural steel, steel bar and other products. The company has obtained ISO9001 quality system certification and European CE certification, and provides MTC quality certification according to EN10204.3.1

Companies adhering to the "integrity, quality, win-win" spirit of enterprise, in the years of pioneering and enterprising, never forget the original aspiration, accumulated strength, with wisdom and sweat to lead the development of iron and steel industry.

The annual production capacity of cold rolled steel plate production line is 600,000 tons, and the production specification is 0.12-1.2mm*750-1250mm. The production line adopts advanced full hydraulic on the road, flexible and stable control, combined with thickness gauge to achieve automatic control of AGC plate thickness, so as to ensure product quality.

TEST ITEMS

Inquiry

Submit