SAE1006 material, belongs to low carbon steel, with high elongation, smooth surface, mirror effect, thickness standard, flat shape, rust resistance and other characteristics, suitable for all kinds of metal stamping and drawing, good performance.

The material of SAE1008 is equivalent to "high-quality carbon structural steel" in China. High-quality carbon structural steel is carbon steel with carbon content less than 0.8%, which contains less sulfur, phosphorus and non-metallic inclusions than carbon structural steel, and has better mechanical properties.

SAE1010 is a carbon structural steel, characterized by low mechanical strength, plasticity, good toughness, it is used to manufacture welding parts with low strength, chemical composition is carbon, silicon, etc. SAE1010 is the American Society of Automotive Engineers standard, the former "10" means that the Mn content is about 1%, the latter "10" means that the average carbon content is 0.1%

Product information:

SAE1006 High speed controlled cold and hot rolling wire delivery status: hot rolling controlled cold standard :Q/ASD18-2004

Chemical composition:

C-0.06  P-0.008  S-0.004 Cr-0.0200  Si-0.04  Mn-0.31  Ni-0.0100  Cu - 0.0040 -

Performance test:

Yield strength :270Mpa

Tensile strength :380Mpa

Elongation :33.5%

SAE1006 Features:

It has the characteristics of high elongation, smooth surface to achieve mirror effect, thickness standard, flat shape, rust resistance, etc., suitable for all kinds of metal stamping, good tensile performance. Such as LED bracket, rotor, lighting, fan, motorcycle fuel tank, steel pipe, household appliances and shell and other hardware products. Adopting SAE1006, the production facilities are equipped with hot-rolled plate surface treatment pickling line, bright hood annealing furnace, four-bar reversible cold rolling, and equipped with plate surface precision levelling unit, stress relief plane tension straightening machine, high precision strip unit

------------------------------------------------------------------------------------------------------------------------------

SAE1008 High speed controlled cold and hot rolling rod delivery status: hot rolling controlled cold

Standard :Q/ASD18-2004

Chemical composition(%):

C-0.06  Si-0.06  Mn-0.38  P-0.009  S-0.006  Cr-0.0100  Ni-0.0100  Cu - 0.0010 -

Performance test:

Yield strength :295-302Mpa,

Tensile strength :394-403Mpa,

Elongation :30-30.5%

This kind of steel has a large output and a wide range of uses, and is generally made of round, square, flat and other profiles, plates and seamless steel pipes by multi-rolling (forging). It is mainly used in the manufacture of general structures and mechanical structures, components, building structures and pipelines for conveying fluids.

------------------------------------------------------------------------------------------------------------------------------

SAE1010 Chemical composition(%):

C ：0.08～0.13， Si：0.15～0.35， Mn：0.30～0.60， S ：≤0.050， P ：≤0.040， Cr：≤0.20， Ni：≤0.25， Cu：≤0.25

1010 steel is a high-quality carbon structural steel, low mechanical strength, plasticity, toughness, cold state easy to die forming, easy to cut processing, good welding performance, in order to improve the surface hardness can be carburized and cyanide treatment. For the manufacture of low strength welding parts, cold stamping parts, forgings and carburized parts such as bolts, washers, partitions, shells, etc.